| 摘要 |
PURPOSE: A conductive electrode paste composition is provided to be sintered at low temperatures, thereby being applied to tempered glass, and forming electrode patterns without organic materials in tempered glass substrate. CONSTITUTION: A conductive electrode paste composition comprises silver powder, silver compound powder, and glass particles of which average particle diameter is 0.1-20 micron, and having a softening point under 300°C or less. The content of the glass particles is 0.1-20 weight% based on 100.0 parts by weight of the silver powder and silver compound powder. A manufacturing method of the conductive electrode paste composition comprises: a step of printing the composition on a substrate; a step of drying the printed substrate in a drying furnace at 150°C or less; and a step of sintering the dried substrate in the drying furnace at 350°C or less. [Reference numerals] (AA) Printing a composition on a substrate; (BB) Drying in a drying furnace at about 150°C; (CC) Sintering in a sintering furnace at below 350°C; (DD) Forming a conductive electrode |