| 摘要 |
<p>A high strength galvanized steel sheet having a tensile strength TS of 590 MPa or more and exhibiting excellent workability (elongation and stretch flangeability) and a method for manufacturing the same are provided. A high strength galvanized steel sheet with excellent workability, characterized by having a component composition containing C: 0.04% or more, and 0.15% or less, Si: 0.7% or more, and 2.3% or less, Mn: 0.8% or more, and 2.2% or less, P: 0.1% or less, S: 0.01% or less, Al: 0.1% or less, N: 0.008% or less, and the remainder composed of iron and incidental impurities on a percent by mass basis, and a microstructure including 70% or more of ferrite phase, 2% or more, and 10% or less of bainite phase, and 0% or more, and 12% or less of pearlite phase on an area fraction basis and 1% or more, and 8% or less of retained austenite phase on a volume fraction basis, wherein an average crystal grain diameter of ferrite is 18 µm or less and an average crystal grain diameter of retained austenite is 2 µm or less.</p> |