WELD METAL HAVING EXCELLENT RESISTANCE TO HYDROGEN EMBRITTLEMENT |
摘要 |
The weld metal of the present invention is formed by gas shield arc welding using a flux-cored wire, has a predetermined chemical component composition, and contains 20% or more of Ti. The amount of Ti-containing oxide particles having a circle-equivalent diameter of 0.15 - 1.0 µm is at least 5000 per square mm, the amount of V per total mass of weld metal present as a compound within the weld metal is 0.002% or more, and the average circle equivalent diameter of V-containing carbide present in the weld metal is 15 nm or less. |