A multi-phase steel including in % wt. C: 0.14-0.25%, Mn: 1.7-2.5%, Si: 0.2-0.7%, Al: 0.5-1.5%, Cr: <0.1%, Mo: <0.05%, Nb: 0.02-0.06%, S: up to 0.01%, P: up to 0.02%, N: up to 0.01% and optionally at least one of Ti, B, and V according to the following stipulation: Ti: up to 0.1%, B: up to 0.002%, V: up to 0.15%, with the remainder iron and unavoidable impurities, wherein the microstructure has at least 10% vol. ferrite and at least 6% vol. residual austenite and the steel has a tensile strength Rm of at least 950 MPa, a yield point ReL of at least 500 MPa and an elongation at break A80 measured in the transverse direction of at least 15%. A method of producing the multi-phase steel.
|