Flux-Cored Arc Welding Wire for Providing Superior Toughness and Weldability to a Welded Joint at a Low Temperature, and Welded Joint Using Same

摘要

Provided are a flux cored arc welding wire able to improve low-temperature toughness of a weld joint and a weld joint using the same, in which the flux cored arc welding wire includes 0.01 wt % to 0.1 wt % of carbon (C), 0.3 wt % to 1.4 wt % of silicon (Si), 1.0 wt % to 3.0 wt % of manganese (Mn), 4.0 wt % to 7.5 wt % of titanium (Ti)+TiO, 0.01 wt % to 3.0 wt % of nickel (Ni), 0.01 wt % to 0.2 wt % of boron (B), 0.02 wt % to 0.42 wt % of yttrium (Y) or 0.02 wt % to 0.56 wt % of a rare earth metal (REM), and iron (Fe) as well as other unavoidable impurities as a remainder.