| 摘要 |
Cu-Ni-Si-Co copper alloy strip having excellent balance between strength and electrical conductivity which can prevent the drooping curl is provided. The copper alloy strip for an electronic materials contains 1.0-2.5% by mass of Ni, 0.5-2.5% by mass of Co, 0.3-1.2% by mass of Si, and the remainder comprising Cu and unavoidable impurities, wherein the copper alloy strip satisfies both of the following (a) and (b) as determined by means of X-ray diffraction pole figure measurement based on a rolled surface: (a) among a diffraction peak intensities obtained by ² scanning at ± = 20° in a {200} pole figure, a peak height at ² angle 145° is not more than 5.2 times that of standard copper powder; (b) among a diffraction peak intensities obtained by ² scanning at ± = 75° in a {111} pole figure, a peak height at ² angle 185° is not less than 3.4 times that of standard copper powder. |