| 摘要 |
<p>The present invention discloses a high-pressure vessel of large size formed with a limited size of e.g. Ni—Cr based precipitation hardenable superalloy. Vessel may have multiple zones. For instance, the high-pressure vessel may be divided into at least three regions with flow-restricting devices and the crystallization region is set higher temperature than other regions. This structure helps to reliably seal both ends of the high-pressure vessel, at the same time, may help to greatly reduce unfavorable precipitation of group III nitride at the bottom of the vessel. Invention also discloses novel procedures to grow crystals with improved purity, transparency and structural quality. Alkali metal-containing mineralizers are charged with minimum exposure to oxygen and moisture until the high-pressure vessel is filled with ammonia. Several methods to reduce oxygen contamination during the process steps are presented. Back etching of seed crystals and a new temperature ramping scheme to improve structural quality are disclosed.</p> |