ANNEALING SEPARATION AGENT FOR PRODUCING GRAIN-ORIENTED SILICON STEEL WITH SMOOTH SURFACE AND GOOD MAGNETIC PROPERTY

摘要

An annealing separator for manufacturing grain-oriented silicon steel with mirror-like surface having good magnetic performance consists of the composition of which is 77-98 by wt% of Al 2 O 3 powder, 1-8 by wt% of alkaline earth powder, 1ˆ¼15 by wt% of alkali metal chloride and/or alkaline earth metal chloride. The annealing separator of the invention can avoid forming a glass-film undercoating on the surface of the steel sheet during high-temperature annealing, and at the same time, the oxide embedded at near-surface of the sheet is removed by means of corrosive reaction of the chloride, so that a produce with smooth surface and stable magnetic performance is obtained.