| 摘要 |
A method for manufacturing a plate inorganic nonmetal material by using a molten slag by introducing the molten slag into a pool for preserving heat and modifying, wherein a temperature of the molten slag is 1450° C.-1600° C., and modifying a viscosity and/or a color of the molten slag according to requirements of the product manufactured. The modified molten slag is introduced into a float process furnace using tin or tin alloy carrier forming a plate of inorganic nonmetal material which is discharged at 1000-1300° C. The plate is maintained at 600° C.-900° C. for 0.5-2 hours in a non-reducing atmosphere, and then cooled to a room temperature within 1-2 hours. An energy-saving and efficient method for comprehensively utilizing the blast furnace slag is provided. The produced plate inorganic nonmetal material has such characteristics as stable color quality, abrasion resistance, pressure resistance, strong adhesiveness, low coefficient of expansion and low shrinkage ratio.
|