To provide a polyarylene sulfide resin composition which contains decreased amount of chlorine, which has a high fluidity and generates small flashes at the time of molding, which has an excellent heat resistance, which can resist heat-processing under the condition of a high temperature, which has moldability at a low mold temperature, a molded article of which has an extremely small change in surface hue before and after reflow, and which is useful for use of injection-molded electronic parts (especially connector), etc. The polyarylene sulfide resin composition is obtained by blending: 100 parts by weight of a polyarylene sulfide resin (A) containing 500 to 2,000 ppm of chlorine and having 10 to 200 Pa · s of melt viscosity (at 310°C and shear rate of 1200 sec -1 ), 10 to 100 parts by weight of a liquid crystalline polyester amide resin (B), and 5 to 250 parts by weight of glass fiber (C) containing 100 ppm or less of nitrogen, and having a total chlorine content of 950 ppm or less.
|