| 摘要 |
<p>Provided is a production method for a transparent double-sided adhesive sheet having little variation in the storage modulus therefor caused by temperature variation, and also having few residual monomers. The production method for the transparent double-sided adhesive sheet, whereby the transparent double-sided adhesive sheet having both sides of a light-permeable film peeled away fulfills prescribed conditions, is a production method for the transparent double-sided adhesive sheet obtained by curing a photo-curable resin composition, and has: a step (1) in which the photo-curable resin composition is coated upon a light-permeable film (Y), and a resin layer having a thickness of 0.01-3 mm is formed; a step (2) in which a light-permeable film (Z) is laminated on the formed resin layer; a step (3) in which a black light is irradiated at 10-300 mJ/cm2 on to a laminate obtained by laminating; and a step (4) in which active energy rays are irradiated at an irradiation amount of 500-5,000 mJ/cm2 on to the laminate having had the black light irradiated thereon.</p> |