摘要 |
A method for producing superalloy weld wire and weld wire having fewer inclusions, and specifically fewer hafnia inclusions, and superalloy weld wire, particularly hafnium-containing superalloy weld wire, produced by this method. The method includes producing directionally solidified cast rod in a diameter of less than about ½ inch. The rod preferably is produced by investment casting or by continuous casting. The directional solidification process results in rod having inclusions such as oxides and dirt segregated into portions of the casting where they are easily removed. The cast rod can then be formed into semi-finished weld wire using a single extrusion step, followed by grinding to the final required diameter.
|