METHOD OF PRODUCING COLD-ROLLED STEEL SHEET AS WELL AS COLD-ROLLED STEEL SHEET AND MEMBERS FOR AUTOMOBILE

摘要

In a method of producing a cold-rolled steel sheet being excellent in not only the phosphate treatability but also the corrosion resistance after coating under severe corrosion environment such as hot salt water immersion test or composite cycle corrosion test, a continuously annealed steel sheet after cold rolling preferably including 0.5-3.0 mass % of Si is pickled to remove a Si-containing oxide layer on a surface layer of the steel sheet and further repickled so that a surface covering ratio of an iron-based oxide on the surface of the steel sheet is not more than 40% and preferably a maximum thickness of the iron-based oxide is not more than 150 nm, as well as a cold-rolled steel sheet produced by this method and a member for automobile using the cold-rolled steel sheet.