Prepare an extruded polymeric foam using a foamable polymer composition that contains a polymer composition with styrene-acrylonitrile copolymer, a blowing agent composition with only 1,1,1,2-tetrafluoroethane (74-78 weight-percent), carbon dioxide (13-16 weight-percent) and water (7-9 weight-percent) where the concentrations are relative to total blowing agent weight, and less than 0.5 weight-percent filler based on foamable polymer composition weight by using an extrusion foaming process with a foaming temperature of 120-125 degrees Celsius to produce a polymeric foam having a density of 29-37 kilograms per cubic meter and a vertical compressive strength in kilopascals having a magnitude exceeding 520 less than the product of the magnitude of the foam density in kilograms per cubic meter and 25.9. |