| 摘要 |
PROBLEM TO BE SOLVED: To provide a high-strength thin steel sheet that is excellent in workability and shows a controlled yield point elongation after accelerated aging, and an advantageous method for manufacturing the same.SOLUTION: A high-strength thin steel sheet has a composition comprising, by mass%, 0.05-0.20% C, ≤0.10% Si, 0.2-1.7% Mn, ≤0.10% P, ≤0.10% S, 0.01-0.10% Al, ≤0.010% N and the balance being Fe and unavoidable impurities, while satisfying a relation: [%Mn]/[%C]≥2.0, wherein [%M] represents the content of element M(mass%) in the steel, and has a tensile strength (TS) of 390 MPa or more, an elongation (EL) of 30% or more and a yield point elongation (YP-EL) after accelerated aging of 1.0% or more. |