| 摘要 |
Polyglycolic acid particles comprising polyglycolic acid having (a) at least 70% by mol of a glycolic acid repeating unit, (b) Mw of 30,000 to 800,000, (c) Mw/Mn of 1.5 to 4.0, (d) a melting point of 197 to 245° C. and (e) a melt crystallization temperature TC2 of 130 to 195° C., and having (i) an average particle diameter (D50) of 3 to 50 mum, and preferably having (ii) D90/D10 of 1.1 to 12, a production process of the particles, including a solution-forming step of dissolving polyglycolic acid in an aprotic polar organic solvent at 150 to 240° C.; a cooling step of cooling the solution to 140° C. or lower at a rate less than 20° C./min to obtain a suspension of polyglycolic acid particles; and a separation step, and a slurry, (powder) coating or toner containing the particles. |