发明名称 |
RESIN COMPOSITION FOR POLYOLEFIN RESIN FOAM, POLYOLEFIN RESIN FOAM AND FOAMED SEALING MATERIAL |
摘要 |
The present invention relates to a resin composition for a polyolefin resin foam, including: a polyolefin (A) having a melt flow rate (MFR) at a temperature of 230° C. of 0.2 to 0.7 g/10 min and a melt tension at break measured at a temperature of 190° C. of 30 cN or more; and a polyolefin (B) having a melt flow rate (MFR) at a temperature of 230° C. of 1.5 to 10 g/10 min and a melt tension at break measured at a temperature of 190° C. of 10 cN or more, in which the polyolefin (B) is contained in an amount of from 15 to 75 parts by weight based on 100 parts by weight of the polyolefin (A).
|
申请公布号 |
US2013079430(A1) |
申请公布日期 |
2013.03.28 |
申请号 |
US201213560399 |
申请日期 |
2012.07.27 |
申请人 |
JINTOKU NAOMI;HATANAKA ITSUHIRO;KOBAYASHI TETSUROU;NITTO DENKO CORPORATION |
发明人 |
JINTOKU NAOMI;HATANAKA ITSUHIRO;KOBAYASHI TETSUROU |
分类号 |
C08L23/12 |
主分类号 |
C08L23/12 |
代理机构 |
|
代理人 |
|
主权项 |
|
地址 |
|