METHOD OF STRENGTHENING VITREOUS MATERIALS

摘要

1,237,394. Strengthening vitreous materials. GLAVERBEL. 19 March, 1968 [27 April, 1967], No. 13246/68. Headings C1A, C1M and C1N. A layer of vitreous or vitro-crystalline material is strengthened by covering the layer while in the solid state either entirely or at zones which are laterally opposed with respect to a mid-surface of the layer with a solid coating(s) in which compressive stresses can be produced or increased by chemically modifying the coating in heated condition while the coating(s) remain solid, with the aid of a reactant in contact therewith and then cooling the coating(s). The coating(s) are preferably from 1 to 150 microns thick and the layer may be less than 3 mm. thick. The chemical modification may involve the combination of an element or compound in the coating(s) preferably of invariable valency e.g. Sn, Ti, Si, V, Pb, Mn, Al, Zr, Th, Bi, Ni, or SiO, TiO, SnO, PbO with another substance e.g. oxidation with ozone or molten KNO 3 , or combination with S, Te, Se or another element the ions of which have a greater ionic radius than oxygen. The chemical modification may involve an ion-exchange e.g. of alkali metal ions between the coating(s) and a contacting medium e.g. the replacement of Na+ in the glass coating(s) by K+ at a temperature below the annealing point of the glass, or the replacement of Na+ in the glass by Li+ at a temperature above the annealing point and confers a lower coefficient of thermal expansion on the glass coating. In the examples (i) a titanium film was deposited by vacuum evaporation on both surfaces of a soda lime glass disc and the film was oxidized with ozone at 550‹ C.; (ii) a SnO film was deposited on the internal and external surfaces of a soda lime glass beaker from an alkaline solution of stannous chloride, and the film was oxidized with molten KNO 3 at 500‹ C.; (iii) a sheet of partially devitrified glass composed by weight of Li 2 O 15%, Al 2 O 3 10%, SiO 2 , 50%, CaO 10%, B 2 O 3 , 8%, TiO 2 7% was coated on both faces with an 80: 20 mixture of germanium and sodium by vacuum deposition. The coated sheet was then exposed to H 2 S and the germanium was sulphurized by the sodium polysulphides formed. The resultant coating(s) are vitreous and pale red and are a mixture of GeS 2 and Na 2 S; (iv) vitreous layers of GeS 2 , CdS, Na 2 S formed by sulphurizing the respective metal on both surfaces of a sodalime glass sheet were immersed in a bath of KCl and NaCl and resulted in a substitution of Na+ by K+ in the vitreous coatings and surface layers of the glass sheet; (v) an enamel comprising the following molecular proportions SiO 2 40, B 2 O 3 10, PbO 25, PbF 2 5, NaF 10, ZrO 2 3, CdO 7 and containing 2% by weight zinc powder was deposited on both faces of the devitrified glass of the composition above and was exposed to dry hydrogen selenide gas at 400‹ C. The zinc in the coating reacted to form ZnSe which was in the vitreous state.