摘要 |
A transparent and flame-retardant aromatic polycarbonate resin composite is provided. A transparent and flame-retardant aromatic polycarbonate resin composite includes (A) 100 parts by mass of a transparent aromatic polycarbonate resin composed of 99 percent by mass to 50 percent by mass of an aromatic polycarbonate resin-A with a viscosity-average molecular weight (Mv) of 3x10 3 to 2.5x10 4 , and 1 percent by mass to 50 percent by mass of an aromatic polycarbonate resin-B with a viscosity-average molecular weight (Mv) of 5x10 4 to 9x10 4 , and, (B) 5x10 -3 parts by mass to 9x10 -2 parts by mass of a flame retardant composed of an alkali metal salt of an organic sulfonic acid, wherein a Q-value is 0.1 cm 3 /sec or smaller, a test piece for UL testing of 2.0 mm thickness molded using the aromatic polycarbonate resin composite satisfies UL94V-0, and, a molded article of 3.0 mm thickness shows a haze value of 2% or smaller. |