| 摘要 |
A galvanized steel sheet having excellent formability is provided including steel having a composition which contains, on a percent by mass basis, 0.03% to 0.15% of C, less than 0.5% of Si, 1.0% to 2.5% of Mn, 0.05% or less of P, 0.01% or less of S, 0.05% or less of Al, 0.0050% or less of N, 0.05% to 0.8% of Cr, 0.01% to 0.1% of V, and the balance being Fe and inevitable impurities; and a zinc plating film on a surface of a steel sheet, and wherein a microstructure of the steel contains ferrite having an average grain diameter of 15 μm or less and 5% to 40% of martensite in an area ratio, and the ratio of martensite having an aspect ratio of less than 3.0 to all the martensite is more than 95% in area ratio.
|