The present invention relates to the development of an alloy material with significantly improved low-temperature brittleness, recrystallization brittleness, and irradiation brittleness by the introduction ofa recrystallization microstructure into an alloy, particularly a tungsten material, to significantly strengthen a weak grain boundary of the recrystallization microstructure. The present invention comprises the steps of: mechanically alloying at least one species selected from a group-IVA, VA, or VIA transition metal carbide and a metallic raw material; sintering base powders obtained through the mechanically alloying step, by using a hot isostatic press; and performing plastic deformation of at least 60% on the alloy obtained through the sintering step, at a strain rate between 10-5s-1 and 10-2s-1 and at a temperature between 500°C and 2,000°C. It is therefore possible to obtain an alloy material with significantly improved low-temperature brittleness, recrystallization brittleness, and irradiation brittleness. |