WELDING ALLOY AND ARTICLES FOR USE IN WELDING, WELDMENTS AND METHOD FOR PRODUCING WELDMENTS

摘要

A nickel, chromium, iron alloy and method for use in producing weld deposits and weldments formed therefrom. The alloy comprises, in weight percent, about 28.5 to 31.0% chromium; about 0 to 16% iron; less than about 1.0% manganese; about 2.1 to 4.0% niobium plus tantalum; 1.0 to 6.5% molybdenum; less than 0.50% silicon; 0.01 to 0.35% titanium; 0 to 0.25% aluminum; less than 1.0% copper; less than 1.0% tungsten; less than 0.5% cobalt; less than about 0.10% zirconium; less than about 0.01% sulfur; less than 0.01% boron; less than 0.03% carbon; less than about 0.02% phosphorous; 0.002 to 0.015% magnesium plus calcium; and balance nickel and incidental impurities. The method includes the steps of forming a welding electrode from the above alloy composition and melting the electrode to form a weld deposit. A preferred weldment may be in the form of a tubesheet of a nuclear reactor.