| 摘要 |
<p>The invention relates to a process for manufacturing a refractory product, comprising the following successive steps: a) mixing of raw materials so as to form a suitable feedstock so that the block obtained in step d) comprises more than 85% of ZrO2, b) melting of said feedstock until a molten material is obtained, c) optionally, casting said molten material, d) cooling of the molten material to solidification in the form of a block, e) optionally, heat treatment, process comprising a compression operation in which a compression pressure of greater than 0.2 MPa is applied to at least one portion of the outer surface of the block obtained in step d), the compression operation beginning at a temperature above the temperature at which, in said block, tetragonal zirconia is converted to monoclinic zirconia or "phase transformation temperature", and ending at a temperature below said phase transformation temperature.</p> |