Disclosed are a composite oxide which is capable of maintaining a large volume of pores even used in a high temperature environment, and which has excellent heat resistance and catalytic activity, as well as a method for producing the composite oxide and a catalyst for exhaust gas purification employing the composite oxide. The composite oxide contains cerium and at least one element selected from aluminum, silicon, or rare earth metals other than cerium and including yttrium, at a mass ratio of 85:15 to 99:1 in terms oxides, and has a property of exhibiting a not less than 0.30 cm3/g, preferably not less than 0.40 cm3/g volume of pores with a diameter of not larger than 200 nm, after calcination at 900° C. for 5 hours, and is suitable for a co-catalyst in a catalyst for vehicle exhaust gas purification. |