| 摘要 |
A flame-retardant polyolefin resin composition was provided excellent in flame retardance, abrasion resistance, flexibility, low-temperature characteristics, mechanical characteristics such as tensile strength and elongation at break, and heat resistance. The flame-retardant polyolefin resin composition of the present invention comprising 100 parts by weight of a polyolefin (A) and 50 to 400 parts by weight of an inorganic flame retarding agent (B), wherein the polyolefin resin composition (A) comprises 30 to 94% by weight of a polypropylene resin (A-1), 1 to 30% by weight of a low-density polyethylene (A-2) in which the number of terminal vinyl groups per 1000 carbon atoms is 0.2 or more, and 5 to 40% by weight of a modified styrene thermoplastic elastomer (A-3) that possesses 0.4% by weight or more of a carboxylic acid group or an acid anhydride group. |