<p>Provided is a steel plate having excellent resistance to brittle crack initiation in a parent material zone and a weld heat affected zone. More particularly, the present invention relates to a high-strength steel sheet having excellent resistance to brittle crack initiation which includes 0.02 wt% to 0.06 wt% of carbon (C), 0.1 wt% or less of silicon (Si), 1.5 wt% to 2.0 wt% of manganese (Mn), 0.012 wt% or less of phosphorous (P), 0.003 wt% or less of sulfur (S), 0.5 wt% to 1.5 wt% of nickel (Ni), 0.003 wt% to 0.015 wt% of aluminum (Al), 0.005 wt% to 0.02 wt% of titanium (Ti), 0.005 wt% to 0.015 wt% of niobium (Nb), 0.002 wt% to 0.006 wt% of nitrogen (N), and iron (Fe) as well as unavoidable impurities as a remainder, and has a value of C+0.5Si-0.1Ni+6Al+3Nb of 0.1% or less, and a method of manufacturing the high-strength steel sheet.</p> |