The method of production of granulated polymer-asphalt binder and sulphur concrete with the participation of sulfur polymer obtained through solvent-borne modification of waste sulfur at the temperature of 135-150° C. consists in composing this sulfur polymer with other ingredients. At the production of granulated polymer-asphalt binder the content of the sulfur polymer amounts to 40-60% by weight which, after heating to the temperature of 135-150° C., is mixed (mixer 2) with 20-40% by weight of waste phosphogypsum and after they are mixed, 15-20% by weight of D-50 road asphalt is dosed, which dissolves in this mixture reacting partly with the sulfur polymer. Next, this mixture is cooled to plastic form and granules of polymer-asphalt binder are formed in the extruder, which fall into 5% solution of silicone emulsion where they are cooled and covered with a layer of silicone emulsion. At the production of sulfur concrete at the temperature of 135-150° C., sulfur polymer in the amount of 25-35% by weight is mixed with waste phosphogypsum in the amount of 10-20% by weight (mixer 2); then the material flows downwards where it is mixed (mixer 1) with hot mineral material and waste slag from copper smelting. Liquid sulfur concrete, which is cooled and crushed into grains of 0-1 cm or poured into molds, is formed. The produced polymer-asphalt binder is used for making a binder course in road surfaces and for road repairs. The produced sulfur concrete is used for basic foundations in road surfaces. |