摘要 |
A method of making an electrochemical cell electrode substrate includes creating an aqueous or dry mixture of chopped carbon fibers, chopped cross-linkable resin fibers that are still fuseable after being formed into a felt, such as novolac, a temporary binder, such as polyvinyl alcohol fiber or powder, forming a non-woven felt from either an aqueous suspension of the aqueous mixture or an air suspension of the dry mixture, by a non-woven, wet-lay or dry-lay, respectively, felt forming process, a resin curing agent, such as hexamethylene tetramine may be included in the aqueous or dry mixture, or it may be coated onto the formed felt; pressing one or more layers of the formed felt for 1-5 minutes to a controlled thickness and a controlled porosity at a temperature at which the resin melts, cross-links and then cures, such as 150° C.-200° C.; and heat treating the pressed felt in a substantially inert atmosphere, first to 750° C.-1000° C. and then to 1000° C.-3000° C. |