Silver powder and method for producing same

摘要

After a reducing agent is added to a water reaction system containing silver ions to deposit silver particles by reduction, the silver particles are dried to obtain a silver powder which is heat-treated at a temperature of higher than 100° C. and lower than 400° C. The silver powder thus heat-treated has a maximum coefficient of thermal expansion of not greater than 1.5% at a temperature of 50° C. to 800° C., and has no heating peak when the silver powder is heated from 50° C. to 800° C. The silver powder has an ignition loss of not greater than 1.0% when the silver powder is ignited until the weight of the silver powder is constant at 800° C. The silver powder has a tap density of not less than 2 g/cm3 and a BET specific surface area of not greater than 5 m2/g.