| 摘要 |
The neutral glass according to the present invention is characterized by excellent hydrolytic stability, a relatively low processing temperature and low content of boron oxide. Here, the neutral glass has the following composition, in percent by weight based on oxide content: SiO2, 70-79; B2O3, 0-<5; Al2O3, <5; ZrO2, 0.5-<5; TiO2, 0.5-6; Na2O, 1-6; K2O, 3 to 8; and Li2O, 0-0.5, wherein a total amount of SiO2 and B2O3 is less than 83 percent by weight. |