| 摘要 |
A ceramic composition is prepared to contain a B2O3—SiO2—Al2O3-MO based glass composition (M: Ca, Mg, Sr and/or Ba, B2O3: 4 to 17.5 weight %, SiO2: 28 to 50 weight %, Al2O3: 0 to 20 weight %, and MO: 36 to 50 weight %): 24 to 40 weight %, SrTiO3 and/or CaTiO3: 46 to 75.4 weight %, CuO: 0.1 to 5.0 weight %, CaO: 0.5 to 7.0 weight %, and MnO, ZnO and/or CoO: 10 weight % or more (however, including 0% by weight). The ceramic composition is subjected to firing to produce a ceramic sintered body, and obtain a composite LC component including the ceramic sintered body. While suppressing the shrinkage behavior during firing, dielectric properties can be improved dramatically as compared with conventional cases, and moreover reliability can be ensured. |