摘要 |
An ultraviolet ray hardening resin composite type coating agent for being applied to a print pattern of a water pressure transfer film to restore an adhesion and including a photo-polymerization oligomer, a photo-polymerization monomer and a photo-polymerization initiator for improving a membrane strength, a chemical resistance and light resistance, said photo-polymerization oligomer including a multi-functional oligomer and a bi-functional oligomer, said photo-polymerization monomer being a bi-functional monomer, said coating agent including a non-reactive resin added in addition to said ultraviolet ray hardening resin composite, said photo-polymerization oligomer being blended at 25 to 56 weight %, said photo-polymerization monomer being blended at 33 to 65 weight %, said photo-polymerization initiator being blended at 5 to 10 weight % and said non-reactive resin being blended at 2 to 10 weight %. |