| 摘要 |
Polyurethane prepolymers are described which are prepared from 2,4′-diiso-cyanate diphenylmethane (2,4′-MDI), a polyol component and an aliphatic diisocyanate. These prepolymers can be cured with aliphatic, cycloaliphatic and/or aromatic amines to form a cured urethane elastomer. In comparison to cured urethane elastomers based on monomeric 2,4′-MDI, these prepolymers provide elastomers with extended pour life, i.e. they exhibit a slower rate of viscosity buildup after curative and prepolymer are mixed which results in a reduced propensity to crack during the curing process and gives the opportunity to cast larger parts. In comparison to polyurea/urethanes prepared from cured TDI-prepolymers and which optionally include H12-MDI, the prepolymers of the invention have better health and safety aspects. |