| 摘要 |
A composition is disclosed, comprising, based on the total weight of the composition, a combination of from 44 to 80 weight percent of a thermoplastic poly(butylene terephthalate); from 20 to 50 weight percent of a thermoplastic poly(ethylene terephthalate) having an intrinsic viscosity of 0.5 to 0.8 deciliters per gram, measured in a 60:40 by weight phenol/1,1,2,2-tetrachloroethane mixture at 23° C. using a relative viscometer operating with a closed loop system, which measures the solvent and sample viscosity simultaneously; from 5 to less than 20 weight percent of a talc filler having an average largest dimension of less than 0.9 micrometers, a median particle size of less than 0.9 micrometers, or both; and from 0.1 to 0.5 weight percent of a mold release agent. The compositions are useful in the manufacture of lighting articles, which can be directly metallized without the inclusion of a base coat. |