| 摘要 |
<p>An object of the present invention is to provide an airbag module ensuring that when an airbag fabricated using a fabric composed of a polyamide yarn excellent in heat resistance is deployed by an inflator gas, the deployment occurs without loss of the gas and an excessive amount of generated gas is not necessary, as a result, the inflator is reduced in weight, and the airbag module of the present invention comprises an airbag fabric composed of a polyamide yarn, wherein the air permeability of the fabric under a pressure of 200 kPa is from 10 to 200 cc/cm 2 /sec and in the thermal stress of the constituent yarn as measured under the conditions of an initial load of 0.02 cN/dtex, a yarn length of 25 cm and a temperature rise rate of 80°C/min, the summed thermal stress of the total of the warp yarn and the weft yarn at 230°C is from 0.33 to 1.20 cN/dtex.</p> |