Method of preparation of talcum product with high purity degree

摘要

The method which is the subject of protection is characteristic by the fact that firstly is made the suspension consisting of 10 to 20 mass % of mineral talc and 80 to 90 mass % of water; resulting suspension is homogenized and thereafter is heated to the temperature 50° to 70° C. To heated suspension is then added 37% hydrochloric acid in the amount of 1 to 6 mass % under continuous stirring. After reaching pH 3 to 5 and increasing the temperature up to 85° C., to the suspension is then added concentrated sulphuric acid in the amount of 1 to 5 mass %. The suspension is further maintained at the temperature up to 90° C., then it is chilled to the ambient temperature and thereafter is separated the sediment which is finally dried at the temperature 140° to 160° C. after washing with water and reaching pH 5 to 6.