The present invention relates to a polyolefin composition comprising (A) a crosslinkable polyolefin with hydrolysable silane groups which upon hydrolysation form an acid or a base, characterised in that the acid or base generates a gel content of at least 40% after 40 hours in the 90° C. cross-linking test, wherein the acid or base is added in an amount of 4.5 mmol/kg to an ethylene/vinyltrimethoxysilane copolymer with a MFR2=2 g/10 min, a density of 923 g/cm3, and 2 wt. % of vinyltrimethoxysilane and then is cross-linked in a waterbath at 90° C., and to a polyolefin composition comprising (i) a crosslinkable polyolefin with hydrolysable silane groups, and (ii) a non-polymeric compound with hydrolysable silane groups which upon hydrolysation form an acid or a base, characterised in that the acid or base generates a gel content of at least 40% after 40 hours in the 90° C. cross-linking test, wherein the acid or base is added in an amount of 4.5 mmol/kg to an ethylene/vinyltrimethoxysilane copolymer with a MFR2=2 g/10 min, a density of 923 g/cm3, and 2 wt. % of vinyltrimethoxysilane and then is cross-linked in a waterbath at 90° C. |