PROPYLENE HOMOPOLYMER FOR CAPACITORS

摘要

[Object] To provide a propylene homopolymer suitable for capacitor films having high withstand voltage and a stretched film formed by stretching the propylene homopolymer. [Solution] A propylene homopolymer of the present invention for capacitors satisfies the following requirements (i) to (v) and (ix): (i) the MFR is 1 to 10 g/10 minutes; (ii) the meso pentad fraction (mmm) measured by 13C-NMR is 0.940 to 0.995; (iii) the integrted amount of elution at 90° C. by CFC using o-dichlorobenzene is 0.5% by weight or less; (iv) the melting point measured using DSC is 152° C. or more; (v) the chlorine content is 2 ppm by weight or less; and (ix) in an elution temperature-elution volume curve measured by cross-fractionation chromatography (CFC) using o-dichlorobenzene, the maximum peak has a peak top temperature in the range of 105° C. to 130° C. and half width of 7.0° C. or less.