METHOD FOR PRODUCING ALUMINUM TITANATE CERAMIC SINTERED BODY, AND ALUMINUM TITANATE CERAMIC SINTERED BODY |
摘要 |
<p>The invention is to provide a process for producing an aluminum titanate-based ceramics capable of realizing low thermal expansion and high mechanical strength and having little dimensional change in firing, at a low firing temperature of lower than 1500°C. The invention is a process for producing an aluminum titanate-based ceramics fired body comprising a step of shaping a ceramic plastic rammed earth containing a precursor mixture and an organic-based binder into a predetermined shape, wherein the starting material mixture containing a titanium source powder, an aluminum source powder and a silicon source powder, and
a step of maintaining the shaped ceramics plastic rammed earth within a temperature range of from 900 to 1350°C at a temperature change per hour of from -50 to +50°C/hr for 3 hours or more, followed by heating up to a temperature of 1400°C or higher and firing at the temperature. And the invention is an aluminum titanate-based ceramics fired body that is obtained by the said invention and having a porosity of from 30 to 60%.</p> |
申请公布号 |
KR20110128802(A) |
申请公布日期 |
2011.11.30 |
申请号 |
KR20117016987 |
申请日期 |
2010.02.24 |
申请人 |
SUMITOMO CHEMICAL CO., LTD. |
发明人 |
TOHMA TETSURO;UOE KOUSUKE;YOSHINO HAJIME |
分类号 |
C04B35/478;C04B35/46;C04B35/64 |
主分类号 |
C04B35/478 |
代理机构 |
|
代理人 |
|
主权项 |
|
地址 |
|