摘要 |
The invention relates to a creep-proof and corrosion-resistant nickel-based alloy for the use in high-temperature technology, comprising in wt-% 0.0015 to 0.60 carbon (C) 0.20 to 0.90 nitrogen (N) 22.0 to 32.0 chromium (Cr) 5.0 to 20.0 elements of group 4, 5, and 6 of the periodic table, except Cr 0.03 to 3.0 aluminum (A1) 0.4 to 3.0 silicon (Si) up to 0.15 elements of group 3 of the periodic table, except actinoids up to 0.60 manganese (Mn) up to 14.8 iron (Fe) up to 0.01 boron (B) a maximum of 0.014 phosphorus (P) a maximum of 0.004 sulfur (S) a minimum of 51 nickel (Ni) and/or cobalt (Co) and melting-related impurities.
|