摘要 |
A ferrous sintered multilayer roll-formed bushing having a ferrous sintered sliding material layer which is sinter-bonded to a back metal steel, wherein the ferrous sintered sliding material layer is produced in such a manner that a Fe—C—Cu—Sn based sintered sliding material mixed powder containing at least carbon of 0.40 to 15 wt %, Cu of 13 to 40 wt % and Sn of 0.5 to 10 wt % is preliminarily sinter-bonded to said back metal steel and then finally sinter-bonded by a liquid-phase sintering at high temperatures higher than 1000° C. after bending into a roll. |