Rare earth oxide superconductor and process for producing the same

摘要

RE superconductive layer excelling in Jc and Tc is formed on an interlayer capable of preventing cracking and diffusion of substrate-constituting Ni element into YBCO layer and excelling in crystallinity and surface smoothness. The interlayer is formed by coating a surface of metal substrate with a mixed solution composed of an organometallic acid salt of cerium, an organometallic acid salt of a solid solution formation element capable of forming a solid solution with cerium and an organometallic acid salt of a charge compensation element capable of compensating for a charge mismatch attributed to a difference between the electron valences of respective ions of cerium and the solid solution formation element and subsequently carrying out heat treatment in a reducing atmosphere of 900 to 1200° C. whose pressure ranges from 0.1 Pa to below atmospheric pressure. Thereafter, a rare earth oxide superconductive layer is formed on the interlayer.