DYNAMIC SEAL MEMBER

摘要

A dynamic seal member includes a ternary fluoroelastomer (FKM) and carbon nanofibers. The carbon nanofibers are carbon nanofibers having an average diameter of 10 to 20 nm, or carbon nanofibers having an average diameter of 60 to 110 nm and subjected to a low-temperature heat treatment. The carbon nanofibers having an average diameter of 60 to 110 nm and subjected to the low-temperature heat treatment have a ratio (D/G) of a peak intensity D at around 1300 cm−1 to a peak intensity G at around 1600 cm−1 measured by Raman scattering spectroscopy of more than 0.9 and less than 1.6. The dynamic seal member has a number of cycles to fracture of 10 or more when subjected to a tension fatigue test at a temperature of 200° C., a maximum tensile stress of 2.5 N/mm, and a frequency of 1 Hz. The dynamic seal member exhibits excellent heat resistance and abrasion resistance.