| 摘要 |
<P>PROBLEM TO BE SOLVED: To provide a manufacturing method for an inkjet recording material which does not generate bending cracks when the recording material is bent, of which glossiness and ink absorbency are superior, and which does not cause disturbance on a coated surface or interference fringes. <P>SOLUTION: A porous layer containing at least one layer of a silica particle of which the average secondary particle diameter is 500 nm or lower, a hydrophilic binder, and a crosslinking agent which can bridge the hydrophilic binder is formed on a supporting body. After forming the porous layer, an inorganic particle layer of which the solid content application amount of an inorganic particle is 330 mg/m<SP>2</SP>or lower is provided on the top of the porous layer in the manufacturing method for the inkjet recording material. After forming the porous layer, an application liquid for the inorganic particle layer is applied in an application amount of 90 capacity% or lower by the void volume of the porous layer by a pre-metering type application method. Then, the surface temperature of the inorganic particle layer 5 seconds after the application liquid for the inorganic particle layer has been applied is made 25°C or lower in the manufacturing method for the inkjet recording material. <P>COPYRIGHT: (C)2011,JPO&INPIT |