| 摘要 |
The invention relates to a process for manufacturing a metal strip having a metallic corrosion protection coating, comprising the steps consisting in: making the metal strip pass through a bath of molten metal comprising between 2 and 8 wt % aluminum, 0 to 5 wt % magnesium and up to 0.3 wt % addition elements, the balance being zinc and inevitable impurities, said bath being maintained at a temperature between 350 and 700° C.; then wiping the coated metal strip by means of nozzles spraying a gas on either side of the strip; and then cooling the coating in a controlled manner until it has completely solidified, said cooling being carried out at a rate less than 15° C./s between the temperature on leaving the wiping unit and the start of solidification and then at a rate greater than or equal to 15° C./s between the start and end of its solidification, and also to a metal strip that can be obtained by this process and to a metal part obtained by deformation of this strip.
|