| 摘要 |
The invention is to provide a process capable of producing aluminium magnesium titanate having a small coefficient of thermal expansion at a firing temperature lower than 1500° C. The production process of the invention comprises maintaining a pre-mixture containing a titania source powder, an alumina source powder, a magnesia source powder and a silica source powder within a temperature range of from 1100° C. to 1350° C. for at least 3 hours, followed by heating up to a temperature not lower than 1400° C. and firing at the temperature. The silica source powder is preferably a powder of alkali feldspar. Aluminium magnesium titanate is prepared according to the production process of the invention, and the resulting aluminium magnesium titanate is ground to give an aluminium magnesium titanate powder.
|