| 摘要 |
<p>A process for the preparation of polymer yarns from ultra high molecular weight homopolymers or copolymers, wherein the process includes the following steps: (a) preparing a suspension of a homopolymer or copolymer and a spinning or gelling solvent of a non polar nature at a weight of homopolymer or copolymer to solvent ratio from 2/98 to 30/70, wherein said ultra high molecular weight homopolymer or copolymer is reactor bimodal or multimodal; (b) feeding said homopolymer or copolymer suspension to an extruder; (c) extruding said suspension under gel forming conditions, at a temperature in excess of 150° C., and under inert conditions; (d) spinning the gel obtained from the extrusion so as to obtain non-stretched filaments with diameters of at least 1 mm, at a temperature in excess of 150° C., while maintaining the inert conditions; (e) cooling the non-stretched filament bundles; (f) treating said non-stretched yarn with a second extraction solvent; (g) drying the non-stretched yarn and (h) stretching the dry yarn.</p> |