摘要 |
<p>An aluminum alloy sheet for bottle cans superior in high-temperature properties, the aluminum alloy sheet comprising the following composition: Mn 0.7-1.5% (mass %, also in the following), Mg 0.8-1.7%, Fe 0.1-0.7%, Si 0.05-0.5%, Cu 0.1-0.6%, with the remainder being Al and inevitable impurities, and comprising a crystal structure elongated in a rolling direction and with an average aspect ratio of crystal grains of 3 or more as determined through an examination from above of a part located at the center in the through-thickness direction, wherein the difference between a maximum value and a minimum value of tensile strength in 0°, 45° and 90° directions relative to the rolling direction is 25 MPa or less, and a difference between a maximum value and a minimum value of n values obtained by tensile tests in 0°, 45° and 90° directions relative to the rolling direction is 0.03 or less.</p> |