METHOD FOR PLATING MANDREL BAR WITH Cr AND PROCESS FOR PRODUCING SEAMLESS PIPE USING THE METHOD AND THE MANDREL BAR

摘要

By using a plating bath containing chromic acid: 100 to 250 g/L, sulfate radical: 3.0 to 5.5 g/L, and a catalyst: 100 to 200% (a weight ratio to the chromic acid content) for conducting electroplating, a Cr-plating film which has an increased film crack density is formed on the surface of a mandrel bar base metal, whereby peeling-off of the Cr-plating film can be suppressed in mandrel mill rolling for extending the service life of the mandrel bar.