METHOD OF MANUFACTURING CLOSING MATERIAL OF INORGANIC POLYMER WITH ENHANCED FIBER AND CLOSING MATERIAL THEREOF

摘要

PURPOSE: A method for manufacturing fiber-reinforced flame-retardant inorganic polymer finishing material is provided to improve adhesive force and roughness by securing surface finishing property and to increase durability by preventing damage caused by ultraviolet rays. CONSTITUTION: A method for manufacturing fiber-reinforced flame-retardant inorganic polymer finishing material comprises the steps of: coating glass fiber with 20-100μm diameter of cross section and 3-8mm length with glass fiber while the temperature of pH 3-5 acid solution is maintained at 40-60°C, and mixing thermoplastic fiber and reinforcing fiber to prepare a mixed fiber solution; and mixing the mixed fiber solution with ethylene vinyl acetate, polyvinylacetate, latex, urethane or acryl suspension, and adding a finishing material to the suspension in a weight ratio of 1:3-1:5.